Barium titanate BaTiO3 sputtering target CAS: 12047-27-7 

Barium titanate BaTiO3 Sputtering targets

Shape: Discs, disks, step disk, delta, plate, sheets or made per drawing

Diameter: 355.6mm (14") max.

Single piece Size: Length: <500mm, Width: <250mm, Thickness: >1mm, if larger size than this, we can do it as Tiles joint by 45 degree or 90 degree

Made sputtering targets method: hot pressing (HP), hot/cold isostatic pressing (HIP, CIP), and vacuum melting, vacuum sintering

Barium titanate is a white powder and transparent as larger crystals. This titanate is a ferroelectric ceramic

 material, with a photorefractive effect and piezoelectric properties. 

Molar mass 233.192 g/mol,            Density: 6.02 g/cm3, 

Melting point: 1625 oC,                 Boiling point: 1750 oC

Technical grade BaTiO3 is produced as a black powder used for the production of vanadium metal and 

ferro vanadium

Applications: 

Barium titanate is a dielectric ceramic used for capacitors. It is a piezoelectric material for microphones

 and other transducers. As a piezoelectric material, it was largely replaced by lead zirconate titanate, also

 known as PZT. Polycrystalline barium titanate displays positive temperature coefficient, making it a 

useful material for thermistors and self-regulating electric heating systems.

Barium titanate crystals find use in nonlinear optics. 

The material has high beam-coupling gain, and can be operated at visible and nearinfrared wavelengths. 

It has the highest reflectivity of the materials used for selfpumped phase conjugation (SPPC) applications. 

It can be used for continuous-wave four-wave mixing with milliwatt-range optical power. 

For photorefractive applications, barium titanate can be doped by various other elements, e.g. iron.

Thin films of barium titanate display electrooptic modulation to frequencies over 40 GHz.

The pyroelectric and ferroelectric properties of barium titanate are used in some types of uncooled sensors

 for thermal cameras.

High purity barium titanate powder is reported to be a key component of new barium titanate capacitor

 energy storage systems for use in electric vehicles